Performance

TEST	Aquence™/Autophoretic® 915/E3	Aquence™/Autophoretic® 800 Series	*ELECTROCOAT
RESIN TYPE	EPOXY/ACRYLIC	PVDC	EPOXY
FILM THICKNESS (MILS)	0.6 - 1.0	0.5 - 1.0	0.6 - 1.0
CROSS HATCH ADHESION	NO FAILURE	NO FAILURE	NO FAILURE
GLOSS @ 60°	40 - 80	5 - 10	30 - 60
PENCIL HARDNESS	H - 3H	4 - 7H	H - 3H
REVERSE IMPACT	60 - 80 IN-LBS	120 - 160 IN-LBS (0.5-0.7 MILS)	40 - 80 IN-LBS
MANDREL TEST (GM9503P)	10	10	2
STONE CHIP (-30° C)	PASS	PASS	PASS
HUMIDITY (1,000 HOURS)	NO FAILURE	NO FAILURE	NO FAILURE
WATER IMMERSION (240 HOURS)	PASS	PASS	PASS
GM 9540P SCRIBE (3MM MAXIMUM CREEP)	32 - 40 CYCLES	40 CYCLES	32 - 40 CYCLES
SAE J2334 SCRIBE (3MM MAXIMUM CREEP)	40 CYCLES	40 CYCLES	40 CYCLES
NEUTRAL SALT SPRAY NO SCRIBE (<10% RUST)	1000 HOURS	>1000 HOURS	>1000 HOURS
TEMPERATURE RESISTANCE	425° F	<250° F	425° F
CURE TEMPERATURE	365° - 395° F	220° F	325° - 375° F
VOC (EPA REFERENCE METHOD 24)	<0.3 LBS/GAL HAPS Compliant	NONE DETECTED	<0.6 LBS/GAL

Note: Initial Cured Film Performance on ACT Cold Rolled Steel Panels, ARP10354. Performance on Production Parts or Other Substrates May Vary.
* Lead-free electrocoat over Zn-phosphate, non-chrome seal rinse, ** Temperature resistance of ACC 800 Series is dependent on exposure duration and airflow conditions. Life cycle testing for parts that will be exposed to more than 200° F is recommended.